| General Information | |
| Material | Cobalt-based, nickel-based and iron-based powder with low oxygen content and controllable powder shape and particle size |
| Specifications | -150/+325 for oxygen-acetylene flame spray welding; -140/+325 for oxygen-acetylene or plasma spray welding;
-60/+200 or-100/+325 for plasma surfacing welding |
| Product feature | Wear resistance, high temperature resistance, thermal shock resistance |
| Application | Oxyacetylene spray welding, spraying, plasma surfacing, spraying and laser spraying, supersonic flame (HVOF) spraying processes;
Metallurgy, Electric power, Glass industry, Paper making and printing, Petrochemical industry, Automobile manufacturing |
Cobalt-Based Welding Powders
1.Major Grades
Co 101F/ERCoCR-C/Cobalt 1 Co 106F/ERCoCR-A/Cobalt 6
Co 112F/ERCoCR-B/Cobalt 12 Co 121F/UNS R30021/Cobalt 21
Co 119F/ERCoCR-G Co 132F/ERCoCR-E
Co 137F/ERCoCR-F
2.Chemical Composition
| Grade | Main Chemical Composition(Weight %) | HRC | Application | International Reference
Standard |
|||
| C | Cr | W | Co | ||||
| Co101F | 2.50 | 31.00 | 12.50 | Bal. | 43-58 | Used for the repair and pre-protection of wear-resistant and firmware powder scouring ore, cylinder valve seat, drill bit and other parts | AWS A5.21
ERCoCr-C |
| Co106F | 1.10 | 29.00 | 4.00 | Bal. | 37-47 | Used in repair and pre-protection of spiracle, valve seats, blade, and spiral push rods, etc. | AWS A5.21
ERCoCr-A |
| Co112F | 1.40 | 29.50 | 8.25 | Bal. | 40-50 | Pre-protection of exhaust valve of internal combustion engine and high temperature and high pressure valve | AWS A5.21
ERCoCr-B |
| Co119F | 3.25 | 26.50 | 14.20 | Bal. | 52-62 | Used to make drill head in petroleum industry | AWS A5.21
ERCoCr-G |
| Co120FB | 2.50 | 32.50 | 17.00 | Bal. | 55-60 | Used for pre-protection of valve seats, blade, wearing panel, rotating sealing ring, etc. | |
| Co121F | 0.25 | 27.30 | ≤0.50 | Bal. | 20-35 | For all kinds of liquid valve, valve seat, turbine blade repair and pre-protection, etc. | AWS A5.21
ERCoCr-E |
| Co132F | 1.55 | 26.00 | 12.00 | Bal. | 36-46 | Used for repair and pre-protection of outlet valve sealing surface and valve seat of internal combustion engines. | AWS A5.21
ERCoCr-F |
| Co137F | 1.00 | 3.00 | 9.00 | Bal. | 40-50 | Used in sawteeth pre-protection and repair, and used to make shear blade, spiral push rods, ect. | |
| Co158F | 0.90 | 26.00 | 5.50 | Bal. | 40-46 | Used for repair and pre-protection of high-pressure valve sealing surface, outlet valve of internal combustion engine, etc. | |
Nickel-Based Welding Powders
1.Major Grades
Ni 240F/UNS N99644/ERNiCr-A Ni 250F/UNS N99645/ERNiCr-B Ni 260F/UNS N99646/ERNiCr-C
2.Chemical Composition
| Grade | Main Chemical Composition(Weight %) | HRC | Application | International Reference
Standard |
|||
| Si | Cr | B | Ni | ||||
| Ni212F | 3.60 | 14.05 | 2.90 | Bal. | – | Glass molds and various forming dies | BNi-12 |
| Ni212F-1 | 2.40 | – | 1.10 | Bal. | – | Glass molds and various forming dies | SP22Cu |
| Ni220F | 2.00 | 4.50 | 0.70 | Bal. | 18-22 | Glass molds and various forming dies | |
| Ni220F-1 | 2.20 | 4.00 | 0.70 | Bal. | 20-24 | Glass molds and various forming dies | |
| Ni225F | 3.50 | 10.50 | 1.20 | Bal. | 22-28 | Glass molds and various forming dies | |
| Ni230F | 2.70 | 2.50 | 1.40 | Bal. | 28-32 | Glass molds and various forming dies | |
| Ni235F | 3.20 | 4.50 | 1.60 | Bal. | 33-37 | Glass molds and various forming dies | |
| Ni237F | 3.00 | 4.50 | 1.15 | Bal. | 35-42 | Glass molds and various forming dies | |
| Ni240F | 3.30 | 7.50 | 1.70 | Bal. | 38-42 | Dies, cam, plunger, outlet valve, corrosion-resistant pump, etc. | T527 FZNi-35 |
| Ni245F | 3.60 | 8.50 | 2.00 | Bal. | 42-48 | Feeding spiral, pump shaft, outlet valve sealing surface | |
| Ni250F | 4.00 | 11.00 | 2.30 | Bal. | 47-53 | Feeding spiral, pump shaft, outlet valve sealing surface | |
| Ni255F | 4.00 | 12.00 | 2.70 | Bal. | 53-59 | Dies, cam, plunger, outlet valve, corrosion-resistant pump, etc. | |
| Ni260F | 4.30 | 15.00 | 3.20 | Bal. | 57-62 | Pump shaft, pulpcutter, extruding spirals, drawing roller, cam, pump wing, bush, plunger,
outlet valve, corrosion-resistant pump, etc. |
|
| Ni263F | 4.30 | 15.50 | 3.50 | Bal. | 57-62 | Feeding spiral, pump shaft, outlet valve sealing surface, plunger, ect. | |
| Ni262F | 4.00 | 16.00 | 3.80 | Bal. | 59-65 | Make easily worn parts, such as paper break rollers, relieved teeth, etc. | |
Iron-Based Welding Powders
1.Major Grades
Fe300F/Fe AF-1 Fe355F/ERFECr-A5 Fe 356F/Eatonite 6
2.Chemical Composition
| Grade | Main Chemical Composition(Weight %) | HRC | Application | International Reference Standard | |||
| Cr | Mo | Ni | Fe | ||||
| Fe300F | 15.00 | 15.00 | 4.00 | Bal. | – | Plasma Cladding of Diesel Engine Valve Sealing Surface | Fe AF-1 |
| Fe355F | 29.00 | – | 4.20 | Bal. | 44-48 | Plasma Cladding of Diesel Engine Valve Sealing Surface | ERFECr-A5 |
| Fe356F | 28.00 | 4.50 | 17.00 | Bal. | 38-44 | Eatonite 6 | |
| Fe356FH | 30.50 | 4.50 | 17.00 | Bal. | ≥38 | Plasma Cladding of Diesel Engine Valve Sealing Surface | |
Contact us
How can we help you?
More Products
-
Forged Alloy
Wear Resistant Products -
Powder Metallurgy
Wear Resistant Products -
Precision Casting
Wear Resistant Products -
Centrifugal Casting
Wear Resistant Products